Hong LU
,
Kewei GAO
,
Hui LIU
,
Lijie QIAO
,
Wuyang CHU
材料科学技术（英）
alpha -Ti foil with a protective layer formed on one side was deflected during corrosion in a methanol solution containing 0.6 mol/L KCl and then a tensile stress was generated at or near the metal passive film interface. The in situ TEM observation showed that corrosion process could facilitate dislocation emission and motion. Adding 10% H2O into the methanol solution decreased the passive film-induced stress from 320 MPa to zero, and the susceptibility to SCC measured in slow strain rate tests decreased correspondingly from 98% to zero.